Ọja Apejuwe

● BEECORE welded honeycomb panel has the advantages of light weight and high strength, high temperature and fire resistance, no cracking, optional and easy to install etc. It is widely used in rail transportation, new energy vehicle, military, petrochemical, and ship and furniture industry.

ohun elo

● Rail Transportation Industry

● New Energy Vehicle Industry

● Military Industry

● Petrochemical Industry

● Ship Industry

● Furniture Cabinet

ifigagbaga Anfani

● Light weight and high strength

● High temperature resistance, no cracking

● Optional and easy to install

● Class A1 fire resistance

● Surface high temperature spraying

● Green environmental protection

● BEECORE Honeycomb Composite Panel manufactured by Jiangsu Beecore in Taizhou obtained certification to Bonding Standard DIN 6701 A2, the accreditation for the use of adhesive bonding in the manufacture of rail vehicles and parts of rail vehicles.

ni pato
Imọ-ẹrọ imọ-ẹrọ
No. igbeyewo Standard esi
1 Bending strength Test GB / T1455-2005 155MPa
2 Flat compressive strength Test GB / T1453-2005 5.09MPa
3 Flat tensile strength Test GB / T1452-2005 8.29MPa
4 Roller peeling strength Test GB / T1457-2005 231(N·mm)/mm
5 Fatigue resistance Test Load 0.3-3.6KN, frequency 10Hz, span 236mm, 3 million times Ko si ibajẹ
6 Sound insulation Test ISO10140-2;2010 28dB
7 Thermal conductivity Test GB / T13475-2008 4.8W/(m2·K)
8 Falling ball impact Test  At a distance of 2meters above the sample, a steel ball with a diameter of 50mm and a mass of 500g falls freely, and the depression depth is measured after half an hour ijinle<0.5mm
9 Fire resistance Test BS EN1363-1;2012 When burning for 46minutes, there is no cracking, collapse, damage, flame flaring and other phenomena on the back surface of the sample, and the specimen remains intact
10 160h neutral salt spray test ISO9227-1990 ijinle<0.5mm