J301 iska caabbinta heerkulka PU adhesive
| Iyo meesha Asal ahaan: | Shiinaha |
| Magaca Brand: | QARAXII |
| Details Baako: | Caag caag ah |
| Waqtiga dirida: | Qiyaastii 15 maalmaha shaqada |
| Shuruudaha Payment: | T / T, L / C |
| Supply Kartida: | 10 Ton / Konton Maalintii |
Product Description
Faahfaahin Degdeg ah
● BEECORE PU adhesive J301 is two-component adhesive, mainly used for bonding honeycomb panels, corrugated board products, etc.
Description
● BEECORE adhesive J301 is a two-component adhesive. Component A is composed of a variety of polyols, adhesion enhancers and fillers. The appearance is a yellowish red viscous fluid, and component B is a coarse MDI. It is a brownish yellow transparent viscous liquid.
Codsiyada
● BEECORE Polyurethane composite adhesives are widely used in the construction industry, automobile manufacturing and shipbuilding, such as polyurethane sandwich panels, aluminum honeycomb panels, polystyrene foam panels, fiberglass panels, stone composite panels, metal plates, etc.
Advantage tartanka
● Good flexibility
Strength Xoog isku xirig sareeya
-Wax ku-ool
● Water and heat resistant
sooc
| Cabirrada Farsamada (la tijaabiyey wixii ka hooseeya 20-25 ° C) | |||
| Shayga | Qeybta A | Qeybta B | Isku Darka Kadib |
| Color | yellow to yellowish red | brownish yellow | Cadaan-cad |
| Cufnaanta (g / cm3) | 1.30 ± 0.02 | 1.00 ± 0.02 | 1.15 ± 0.1 |
| State | dheecaan | dheecaan | dheecaan |
| Isugeynta saamiga | 5: 01 | ||
| Isku Darka Kadib | |||
| Work life(100g) | Miinada 50-60 | ||
| Waqtiga lagu talinayo | gudahood 35mins (min isku-darka ilaa dhammaynta) | ||
| Temperature Range for application | 15-35 ° C,45% qoyaan | ||
| Xaraashka Bilowga ah | 5-6 saacadood markay tahay 25 ° C / 60mins 65 ° C | ||
| Waqti si loo gaaro daawo buuxda | 1-2 days under room temperature | ||
| / 24 hours at 60°C keep 60mins | |||
| Awooda diiran | ≥13MPa (60mins at 60°C or 3 days at 25°C) | ||
| Tijaabada VOC | Ku raacsan GB18538 / TB3139 | ||
| Flame Retardant Rating | S4 (DIN5510) | ||