Welded aluminum honeycomb panel for railway, military, oil floating plate

Place of   Origin:

Suzhou, Jiangsu Province, China

Brand Name:

BEECORE

Packaging   Details:

Plywood Case

Delivery Time:

7-15 workdays

Payment Terms:

T/T, L/C, PayPal

Supply Ability:

300 PCS per day

Product Description Back to list

BEECORE welded honeycomb panel has the advantages of light weight and high strength, high temperature and fire resistance, no cracking, optional and easy to install etc. It is widely used in rail transportation, new energy vehicle, military, petrochemical, and ship and furniture industry.


Applications

Rail Transportation Industry

• New Energy Vehicle Industry

• Military Industry

• Petrochemical Industry

• Ship Industry

• Furniture Cabinet


Competitive Advantage

• Light weight and high strength

• High temperature resistance, no cracking

• Optional and easy to install

• Class A1 fire resistance

• Surface high temperature spraying

• Green environmental protection

• BEECORE Honeycomb Composite Panel manufactured by Jiangsu Beecore in Taizhou obtained certification to Bonding Standard DIN 6701 A2, the accreditation for the use of adhesive bonding in the manufacture of rail vehicles and parts of rail vehicles.

Specifications

Technical Data Sheet

No.

Test

Standard

Result

1

Bending strength Test

GB/T1455-2005

155MPa

2

Flat compressive strength Test

GB/T1453-2005

5.09MPa

3

Flat tensile strength Test

GB/T1452-2005

8.29MPa

4

Roller peeling strength Test

GB/T1457-2005

231(N·mm)/mm

5

Fatigue resistance Test

Load 0.3-3.6KN, frequency 10Hz, span 236mm, 3 million times

No damage

6

Sound insulation Test

ISO10140-2;2010

28dB

7

Thermal conductivity Test

GB/T13475-2008

4.8W/(m2·K)

8

Falling ball impact Test 

At a distance of 2meters above the sample, a steel ball with a diameter   of 50mm and a mass of 500g falls freely, and the depression depth is measured   after half an hour

Depth<0.5mm

9

Fire resistance Test

BS EN1363-1;2012

When burning for 46minutes, there is no cracking, collapse, damage,   flame flaring and other phenomena on the back surface of the sample, and the   specimen remains intact

10

160h neutral salt spray test

ISO9227-1990

Depth<0.5mm